Įgyvendinimo standartai: GB/T8162 besiūlis plieninis vamzdis konstrukcijai, GB/T8163 besiūlis plieninis vamzdis skysčiams transportuoti. 0420D ir 0420E mechaninės savybės: tempiamasis stipris 520 ~ 680 MPa,<16 service strength 2420MPa, 16mm~30mm service strength 2400, 230mm Yield strength 2380MPa Impact test Q420D minus 20C Impact energy 234, impact test Q420E minus 40C Impact energy 227 :0.20, chromium: <0.30, nickel: <0.50, copper: 0.20, nitrogen: 0.015, :0.20, aluminum, 20.015.Q420E seamless steel pipe chemical composition: carbon: 0.20, silicon: 0.50, :1.70, phosphorus: 0.025, Sulfur: 0.020, : 0.07, : 0.20, : 0.20 Chromium: <0.30, Nickel: <0.50, Copper: <0.20, Nitrogen: 0.015, : 0.20, Aluminum, 20.015. Steel refining method: Steel should be processed by electric arc furnace Refining outside the furnace or gas converter plus outside refining method. After negotiation between the supply and demand parties, other methods with higher requirements can also be used to treat refining. When the demander requires a certain refining method, it should be stated in the contract.
Vamzdžių gamybos būdas: Vamzdžiai taip pat gali būti gaminami nepertraukiamo liejimo, liejimo formos arba karšto valcavimo būdu.
Ištisinio liejimo vamzdžiai taip pat turi atitikti YB/T 4149 reikalavimus; karšti vamzdžiai taip pat turi atitikti YB/T 5221 arba YB/T 5222 taisykles; liejimo formos vamzdžiai taip pat gali remtis karštų (kaltų) vamzdžių taisyklėmis.